Property
Test Method
40 mil LLDPE
Smooth
80 mil LLDPE
Textured
80 mil LLDPE
Thickness (mils)
Compound Density (g/cc)
Carbon Black Dispersion
Carbon Black Content ( %)
ASTM D 5199
ASTM D 1505
ASTM D 5596
ASTM D 1603
38 (min) /40 (min)
0.939 (max)
Al, A2, A3
2 -3
72 (min) /80 (min)
0.939 (max)
Al, A2, A3
2 -3
72 (min) /80 (min)
0.939 (max)
Al, A2, A3
2 -3
Tensile Properties
1. Ultimate Tensile Strength (ppi)
2. Ultimate Elongation ( %)(2.5" gauge)
ASTM D 6693
ASTM D 6693
140 (min)
650 (min)
304 (min)
800 (min)
169 (min)
300 (min)
Puncture Resistance (lbs.)
ASTM D 4833
55 (min)
112 (min)
96 (min)
Field Seam Properties
1. Shear Strength (ppi)
2. Peel Strength (Inside and outside tracks
for fusion welds)
ASTM D4437 (modified NSF 54)
ASTM D4437 (modified NSF 54)
56 (min)
48 (min), FTB
120 (min)
100 (min), FTB
120 (min)
100 (min), FTB
ame0
TYPICAL PROPERTIES -TABLE 2.01 -A
Notes:
LLDPE refers to Linear Low Density Polyethylene and HDPE refers to High Density Polyethylene.
2 First value represents lowest individual value. Second value represents minimum average roll value.
3 Core Thickness, exclusive of textured surface.
4 Seam strength refers to both fusion and extruded seams for HDPE to HDPE welds.
5 If peel strength exceeds ultimate tensile strength of the sheet but the sample fails FTB, the test will be considered a pass.
6 Federal Test Method Standards.
7 Film Tear Bond (FTB) is defined as failure of one of the sheets by tearing, instead of separating from the other sheet at the weld interface area (sheet fails