1 2 3 4 5 6 7 8 9 10 <br />Thickness ( GRI GM8, as applied by ASTM D 5994) <br />Thickness (mils) 102 105 109 107 108 104 104 101 107 105 <br />105 <br />3 <br />I 101 <br />I <br />« min <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.937 0.937 0.938 <br />0.937 0.001 <br />Carbon Black Content (ASTM D 1603,Mod) <br />% Carbon Black 2.99 2.93 <br />2.96 0.04 <br />Tensile Properties (ASTM D 638 /GRI GM17, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 202 194 195 213 193 <br />TD Yield Strength (ppi) 204 202 207 227 203 <br />MD Break Strength (ppi) 316 321 269 309 302 <br />TD Break Strength (ppi) 246 283 231 268 249 <br />'ID Yield Elongation ( %) 28 24 29 23 23 <br />TD Yield Elongation ( %) 24 24 26 25 25 <br />MD Break Elongation ( %) 623 636 553 585 621 <br />TD Break Elongation ( %) 488 571 458 508 523 <br />199 <br />I 8 <br />10 <br />I 209 <br />303 <br />I 21 <br />20 <br />I 255 <br />25 <br />I <br />3 <br />1 <br />25 I <br />I 604 <br />34 <br />42 <br />509 <br />I <br />2rtu. <br />TRI I Environmental, Inc. <br />A Texas Research International Company <br />Material: Polyflex Single Sided Textured 100 mil LLDPE Geomembrane <br />Sample Identification: LT2 -0 -10- 6031 -3 <br />TRI Log #: E2339 -87-08 <br />PARAMETER <br />MD Machine Direction <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek Mine, Victor Colorado <br />TEST REPLICATE NUMBER <br />STD. <br />DEV. <br />TD Transverse Direction <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 3 of 5 <br />GeosyntheticTesting.com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />MEAN <br />