Laserfiche WebLink
1 2 3 4 5 6 7 8 9 10 <br />Thickness ( GRI GM8, as applied by ASTM D 5994) <br />Thickness (mils) 112 110 105 101 106 103 109 106 108 104 <br />I 106 <br />I 3 <br />« min <br />101 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.936 0.937 0.937 <br />0.001 <br />0.937 <br />Carbon Black Content (ASTM D 1603,Mod) <br />% Carbon Black 2.43 2.48 <br />0.04 <br />2.46 <br />Tensile Properties (ASTM D 638 /GRI GM17, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 212 212 215 227 209 <br />TD Yield Strength (ppi) 202 212 211 217 207 <br />MD Break Strength (ppi) 320 323 217 290 284 <br />TD Break Strength (ppi) 263 255 269 258 245 <br />1 1D Yield Elongation ( %) 22 28 25 25 25 <br />TD Yield Elongation ( %) 24 24 24 26 25 <br />MD Break Elongation ( %) 620 619 400 551 560 <br />TD Break Elongation ( %) 506 488 520 498 466 <br />215 <br />7 <br />6 <br />I 210 <br />287 <br />43 <br />9 <br />I 258 I <br />25 <br />I <br />2 <br />1 <br />I 25 <br />1 550 <br />90 <br />20 <br />496 I <br />Material: Polyflex Single Sided Textured 100 mil LLDPE Geomembrane <br />Sample Identification: LT2 -0-10- 6014 -3 <br />TRI Log #: E2339 -87 -08 <br />PARAMETER <br />MD Machine Direction <br />TRI / Environmental, Inc. <br />A Texas Research International Company <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek Mine, Victor Colorado <br />TEST REPLICATE NUMBER <br />MEAN <br />STD. <br />DEV. <br />TD Transverse Direction <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 2 of 5 <br />GeosyntheticTesting.com <br />9063 Bee Caves Road / Austin, TX 787331512 263 2101 / fax: 512 263 2558 <br />