0 aterial: Poly -flex Textured 100 mil LLDPE Geomembrane <br />Sample Identification: LT2 -0-10- 6253 -3 <br />TRI Log #: E2341 -87 -04 <br />PARAMETER TEST REPLICATE NUMBER <br />1 2 3 4 5 6 7 8 9 10 <br />Thickness (GRI -GM8 via ASTM D 5994) <br />Thickness(mils) 110 116 106 105 104 112 112 114 107 106 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.937 0.937 0.937 <br />Carbon Black Content (ASTM D 1603,mod.) <br />Carbon Black 2.32 2.37 <br />Tensile Properties (ASTM D 638 /GRI GM17, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) <br />TD Yield Strength (ppi) <br />MD Break Strength (ppi) <br />TD Break Strength (ppi) <br />MD Yield Elongation ( %) <br />TD Yield Elongation ( %) <br />MD Break Elongation ( %) <br />TD Break Elongation ( %) <br />TRI / Environmental, Inc. <br />A Texas Research International Company <br />III Machine Direction TD Transverse Direction <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek Mine - Victor Colorado <br />201 222 201 206 205 <br />201 206 198 214 203 <br />265 299 265 285 274 <br />251 206 237 273 205 <br />27 26 24 26 27 <br />26 30 27 25 25 <br />535 555 544 563 528 <br />510 423 479 540 410 <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 2 of 2 <br />Geosyntheti cTesti n g. com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />STD. <br />MEAN DEV. <br />I 109 I <br />104 <br />0.937 <br />2.35 <br />I <br />204 <br />I 278 I <br />234 <br />26 <br />276 <br />I 545 I <br />472 <br />4 <br />« min <br />0.000 <br />0.04 <br />9 <br />6 <br />15 <br />29 <br />1 <br />2 <br />14 <br />56 <br />