Laserfiche WebLink
1 2 3 4 5 6 7 8 9 10 <br />Thickness (GRI GM8, via ASTM D 5994) <br />Thickness (mils) 103 106 109 106 107 110 106 109 106 105 <br />107 <br />I 2 <br />« min <br />103 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.937 0.937 0.937 <br />0.000 <br />0.937 <br />Carbon Black Content (ASTM D 1603, mod.) <br />% Carbon Black 2.62 2.72 <br />0.07 <br />2.67 <br />Tensile Properties (ASTM D 638 /GRI GM17, 2 ipm strain rate, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 198 192 209 205 217 <br />TD Yield Strength (ppi) 208 196 165 199 209 <br />MD Break Strength (ppi) 312 242 321 278 284 <br />TD Break Strength (ppi) 246 248 185 278 276 <br />MD Yield Elongation ( %) 25 24 25 27 25 <br />TD Yield Elongation ( %) 24 23 25 24 25 <br />I D Break Elongation ( %) 623 498 619 563 535 <br />TD Break Elongation ( %) 478 524 395 586 574 <br />204 <br />10 <br />18 <br />I 195 <br />I 287 <br />I 31 <br />38 <br />247 <br />25 <br />I 1 <br />1 <br />I 24 <br />567 <br />54 <br />I 78 <br />I 511 <br />PARAMETER <br />MD Machine Direction <br />TRI I Environmental, Inc. <br />A Texas Research International Company <br />lik aterial: Polyflex 100mil Single Sided TexturedLLDPE Geomembrane <br />Sample Identification: LT2 -0 -10- 6187 -3 <br />TRI Log #: E2341 -03 -03 <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek <br />TEST REPLICATE NUMBER <br />TD Transverse Direction <br />NA Not Available <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 5of7 <br />Geosyntheti cTesti n g. com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />MEAN <br />STD. <br />DEV. <br />