1 2 3 4 5 6 7 8 9 10 <br />Thickness (GRI GM8, via ASTM D 5994) <br />Thickness (mils) 114 113 110 108 98 105 109 113 107 104 <br />108 <br />I 5 <br /><< min <br />I 98 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.935 0.936 0.936 <br />0.001 <br />0.936 <br />Carbon Black Content (ASTM D 1603, mod.) <br />% Carbon Black 2.68 2.76 <br />0.06 <br />2.72 <br />Tensile Properties (ASTM D 638 /GRI GM17, 2 ipm strain rate, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 198 188 203 203 217 <br />TD Yield Strength (ppi) 200 202 199 201 197 <br />MD Break Strength (ppi) 289 303 289 268 298 <br />TD Break Strength (ppi) 218 269 243 264 253 <br />MD Yield Elongation ( %) 24 24 26 26 24 <br />TD Yield Elongation ( %) 23 23 24 23 24 <br />I D Break Elongation ( %) 568 626 571 534 551 <br />TD Break Elongation ( %) 418 538 500 556 519 <br />202 <br />10 <br />2 <br />I 200 <br />I 289 <br />I 13 <br />20 <br />249 <br />25 <br />1 <br />1 <br />I 23 <br />570 <br />35 <br />I 506 <br />I 54 <br />TRI / Environmental, Inc. <br />A Texas Research International Company <br />Ill aterial: Polyflex 100mil Single Sided TexturedLLDPE Geomembrane <br />Sample Identification: LT2 -0 -10- 6120 -3 <br />TRI Log #: E2341 -03 -03 <br />PARAMETER <br />MD Machine Direction <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek <br />TEST REPLICATE NUMBER <br />TD Transverse Direction <br />NA Not Available <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 2 of 7 <br />Geosynth eticTesti n g. com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />STD. <br />MEAN DEV. <br />