1 2 3 4 5 6 7 8 9 10 <br />Thickness (GRI GM8, via ASTM D 5199) <br />Thickness (mils) 123 103 106 104 126 101 107 102 106 105 <br />108 <br />I 9 <br />« min <br />I 101 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.937 0.937 0.938 <br />0.001 <br />0.937 <br />Carbon Black Content (ASTM D 1603, mod.) <br />% Carbon Black 2.23 2.28 <br />0.04 <br />2.26 <br />Tensile Properties (ASTM D 638 /GRI GM17, 2 ipm strain rate, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 227 188 190 182 193 <br />TD Yield Strength (ppi) 209 202 201 242 189 <br />MD Break Strength (ppi) 539 441 413 436 485 <br />TD Break Strength (ppi) 379 477 431 561 452 <br />MD Yield Elongation ( %) 27 28 28 28 27 <br />TD Yield Elongation ( %) 25 25 26 26 25 <br />/ID Break Elongation ( %) 900 869 821 893 919 <br />TD Break Elongation ( %) 765 1001 874 876 944 <br />196 <br />18 <br />20 <br />I 209 <br />463 <br />E <br />50 <br />67 <br />460 <br />28 <br />1 <br />1 <br />I 25 <br />880 <br />38 <br />I <br />I 892 <br />88 <br />TRI / Environmental, Inc. <br />A Texas Research International Company <br />• aterial: Polyflex 100mil smooth LLDPE Geomembrane <br />Sample Identification: LS2 -0 -10- 6200 -3 <br />TRI Log #: E2341 -54 -02 <br />PARAMETER <br />MD Machine Direction <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek <br />TEST REPLICATE NUMBER <br />MEAN <br />STD. <br />DEV. <br />TD Transverse Direction <br />NA Not Available <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 3 of 6 <br />Geosyntheti cTesti n g.com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />