Laserfiche WebLink
1 2 3 4 5 6 7 8 9 10 <br />Thickness (GRI GM8, as applied by ASTM D 5199) <br />Thickness (mils) 111 108 102 101 101 104 102 115 107 107 <br />I 106 <br />I 5 <br />« min <br />101 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.936 0.936 0.936 <br />0.000 <br />0.936 <br />Carbon Black Content (ASTM D 1603,Mod) <br />% Carbon Black 2.53 2.51 <br />0.01 <br />2.52 <br />Tensile Properties (ASTM D 638/GRI GM17, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 190 173 196 184 196 <br />TD Yield Strength (ppi) 210 206 199 200 196 <br />MD Break Strength (ppi) 475 481 486 473 476 <br />TD Break Strength (ppi) 509 514 477 444 496 <br />'ID Yield Elongation ( %) 23 23 23 23 23 <br />TD Yield Elongation ( %) 23 22 22 22 22 <br />MD Break Elongation ( %) 924 1109 923 981 930 <br />TD Break Elongation ( %) 1039 1043 1086 879 1171 <br />I 188 <br />10 <br />( 6 <br />202 <br />I 478 <br />5 <br />I 28 <br />488 <br />23 <br />I <br />0 <br />0 <br />I 22 <br />973 <br />80 <br />I 1044 I <br />106 <br />zrtu. <br />PARAMETER <br />MD Machine Direction <br />TRI I Environmental, Inc. <br />A Texas Research International Company <br />Material: Polyflex Smooth 100 mil LLDPE Geomembrane <br />Sample Identification: LS2 -0 -10- 6067 -3 <br />TRI Log #: E2339 -87 -07 <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC <br />Project: Cripple Creek Mine, Victor Colorado <br />TEST REPLICATE NUMBER <br />MEAN <br />STD. <br />DEV. <br />TD Transverse Direction <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 4 of 5 <br />GeosyntheticTesting.com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />