Laserfiche WebLink
1 2 3 4 5 6 7 8 9 10 <br />Thickness (ASTM D GRI GM8 via ASTM D 5994) <br />Thickness (mils) 84 88 86 87 89 87 88 85 86 84 <br />86 <br />I 2 <br />« min <br />I 84 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.935 0.935 0.935 <br />0.000 <br />0.935 <br />Carbon Black Content (ASTM D 1603,Mod) <br />% Carbon Black 2.67 2.71 <br />0.03 <br />2.69 <br />Tensile Properties (ASTM D 638 /GRI GM17, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 155 172 160 172 166 <br />TD Yield Strength (ppi) 159 173 161 174 166 <br />MD Break Strength (ppi) 268 265 272 304 212 <br />TD Break Strength (ppi) 233 241 188 247 216 <br />MD Yield Elongation ( %) 22 22 22 22 22 <br />O D Yield Elongation ( %) 23 23 23 23 23 <br />MD Break Elongation ( %) 649 593 644 693 489 <br />TD Break Elongation ( %) 584 584 450 586 545 <br />165 <br />I 7 <br />7 <br />I 167 <br />264 <br />I 33 <br />24 <br />I 225 <br />22 <br />I 0 <br />0 <br />I 23 <br />613 I <br />78 <br />I 550 <br />58 <br />M aterial: Poly -flex Single Sided Textured 80 mil. LLDPE Geomembrane <br />Sample Identification: LT2 -8 -10- 6174 -37 <br />TRI Log #: E2341 -56 -08 <br />PARAMETER <br />MD Machine Direction <br />TRI I Environmental, Inc. <br />A Texas Research International Company <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC Earth & Environmental <br />Project: Cripple Creek Mine, Victor Colorado <br />TEST REPLICATE NUMBER <br />STD. <br />MEAN DEV. <br />TO Transverse Direction <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 6 of 7 <br />G eosynth eti cTesti ng. com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />