Laserfiche WebLink
1 2 3 4 5 6 7 8 9 10 <br />Thickness (ASTM D GRI GM8 via ASTM D 5994) <br />Thickness (mils) 80 83 83 83 82 83 84 81 84 86 <br />83 <br />I 2 <br />« min <br />I 80 <br />Density (ASTM D 1505) <br />Density (g /cm3) 0.935 0.935 0.935 <br />0.000 <br />0.935 <br />Carbon Black Content (ASTM D 1603,Mod) <br />Carbon Black 2.74 2.68 <br />0.04 <br />2.71 <br />Tensile Properties (ASTM D 638 /GRI GM17, Type IV specimen - LLDPE) <br />MD Yield Strength (ppi) 172 161 158 161 159 <br />TD Yield Strength (ppi) 160 163 165 178 172 <br />MD Break Strength (ppi) 272 277 265 267 263 <br />TD Break Strength (ppi) 197 215 210 216 227 <br />MD Yield Elongation ( %) 25 21 25 23 23 <br />I D Yield Elongation ( %) 23 23 23 23 23 <br />MD Break Elongation ( %) 600 664 646 641 648 <br />TD Break Elongation ( %) 499 541 528 510 549 <br />162 <br />I 6 <br />7 <br />I 168 <br />269 <br />I 6 <br />11 <br />I 213 <br />23 <br />I 2 <br />0 <br />I 23 <br />640 <br />24 <br />I 525 <br />21 <br />M aterial: Poly -flex Single Sided Textured 80 mil. LLDPE Geomembrane <br />Sample Identification: LT2 -8 -10- 6126 -37 <br />TRI Log #: E2341 -56 -08 <br />PARAMETER <br />MD Machine Direction <br />TRI I Environmental, Inc. <br />A Texas Research International Company <br />GEOMEMBRANE TEST RESULTS <br />TRI Client: AMEC Earth & Environmental <br />Project: Cripple Creek Mine, Victor Colorado <br />TEST REPLICATE NUMBER <br />TD Transverse Direction <br />The testing is based upon accepted industry practice as well as the test method listed. Test results reported herein do not apply <br />to samples other than those tested. TRI neither accepts responsibility for nor makes claim as to the final use and purpose of the material. <br />TRI observes and maintains client confidentiality. TRI limits reproduction of this report, except in full, without prior approval of TRI. <br />page 3 of 7 <br />G eosynth eti cTesti n g. com <br />9063 Bee Caves Road / Austin, TX 78733 / 512 263 2101 / fax: 512 263 2558 <br />I MEAN <br />STD. <br />DEV. <br />