Laserfiche WebLink
TYPICAL PROPERTIES -TABLE 2.01-D <br />o e Test Method 100 mil HDPE Textured 100 mil <br /> HDPE <br />Thickness Imllsl' GRI-GM8 98 (min)/100 Iminl 98 (mini/100 Iminl' <br />Compound Dens(ly (g/cc) ASTM D 1505 0.940 (min) 0.940 Imin) <br />Carbon Black Dispersion ASTM D3015 A1, A2, B1 A1, A2, B1 <br />Carbon 81ack Content (%) ASTM D 1603 2-3 2-3 <br />Tenalle Properties <br />1. Yield Tensile Strength Ippil ASTM D 638, NSF 54 220 (mint 190 (mint <br />2. Ultimata Tenslla Strength Ippp ASTM D 638, NSF 54 380 (mint 220 Imin) <br />3. Yield Elongation 1%) ASTM D 638, NSF 54 12 Iminl 12 (mint <br />4. Ultimate Elongation 1%)(2.5' gauge) ASTM D 638, NSF 54 600 (mint 160 (mint <br />Puncture Resistance fibs.) ASTM D 4833 120 (mint 96 (min) <br />Field Seam Properties' <br />1. Shear Strength Ippll ASTM D4437 (modified NSF 541 200 (mint 200 (min) <br />2. Peel Strength° (Inside and Outside ASTM D4437 (modified NSF 541 130 (mini, FTBss•' 130 (min), FTBs.s.t <br />Tracks for fusion weld) <br />Notes; <br />r HOPE refers to High Density Polyethylene and VLDPE raters to Very Low Density Pnlyetltylena. <br />t Fkst value reprssente lowest Individual value. Saeond value represents minimum average roll value. <br />r Cae Thickness, axeluslve of tostursd eurlace. <br />' Seam strength raters to both luslon and sstruded seams for HDPE to HDPE welds. <br />s II peal strength axeeade ultimate tensile strength of the sheet but the sample tails FTg, ttta test will be considered a pass. <br />r federal Test Method Standards. <br />' Film Tear Bond IFTaI Is delined as lailurs of one of rite attests by tearing, instead of separating Irom the outer sheet at the weld interlace area Ishaet <br />lags halos weldl• <br />March 28, 1996 Section 02776.0 <br />02776.0-12 Gcomembrane <br />Revision 4 <br />