Laserfiche WebLink
TYPICAL PROPERTIES -TABLE 2.01-8 <br />o e Test Method 40 mil HDPE 80 mil HDPE Textured 80 mil <br /> HDPE <br />Thickness Imilsl' GRI-GMB 38 (mini/40 78 Iminl/80 (mini 78 (mint/80 (mint' <br />Compound Density Ig/ccl ASTM D 1505 Iminl 0.940 Imin) 0.940 (mint <br />Carbon Bieck Dispersion ASTM D3015 0.940 (mint A1, A2, B1 A1, A2, B1 <br />Carbon Black Content (%) ASTM D 1603 A1, A2, 81 2-3 2.3 <br /> 2-3 <br />Tenslla Propartlee <br />1. Ylald Tenslla Strength Ippl) ASTM D 638, NSF 54 85 (min) 169 Imin) 169 (min) <br />2. Ultimate Tenslla Strength (ppi) ASTM D 638, NSF 54 152 (mint 304 (mint 169 Imin) <br />3. Yield Elongation (%1 ASTM D 638, NSF 54 12 (mint 12 (min) i 2 Imin) <br />4. Ultimata Elangetlon (%112.6' gauge) ASTM D 638, NSF 54 560 Imin) 560 (min) 160 Imin) <br />Puncture Resistance (Ibs.) ASTM D4833 50 lminl 96 Imin) 96 Imin) <br />Field Saem Properties' <br />1. Sheer Strength (ppll ASTM D 4437 (modified NSF 541 80 Imin) 160 Imin1 160 (mint <br />2. Peel Strength' (Inside and Outside ASTM D 4437 (modified NSF 541 52 (mint. FTBa~' ° 104 Iminl, FTBa'•° 104 Iminl, FTB°~'•° <br />Tracks for lesion weld) <br />Field Seam Properllas° <br />1. Shaer Strength Ippl- ASTM D4437 Imodilied NSF 54i 45 (mint 88 (mint 88 Imin) <br />2. Peal Strength (ppll° (inside and outside ASTM D4437 (modified NSF 541 FTBa•' ° FTBa' ° FTBa.r.e <br />tracks for fusion welds) <br />Norec: <br />HDPE relerc to Hiah Denclty Polyethylene and VLDPE relarc ro Vary Low Dcrtstty Polyethylene. <br />° Firer varus repreeenrt lowest Individual value. Second value represents minimum 'u're'a roll value. <br />' Core Tldckneca, eacluclva or ta^tteed curiae'. <br />' Seam ctranath relarc to both lualon end extruded caemr ror HDPE ro HDPE welds. <br />° Ssam atrenarh reran ro both lualon and ectrudad casms for HDPE to VLDPE welds. <br />° Ir peal ctrenalh e^eoads Wrlmato r'o'lls errangth of the cheat bur the sample tails FTa, the test will be considered a pass. <br />r Fedsrel Teal Merhod StaMarda. <br />° Film Taar Band IFTaI la defined ea taller' or one or the sheets 6y tearing, instead or separating Irom the atlter sheet at fife weld interlace area lstteel tails baler' wcldl, <br />March 26, 1998 Section 02776.0 <br />02778.0-10 Gconternlrrane <br />Revision 4 <br />